Enhanced thermal stability of A1-pillared smectites modified with Ce and La

J. L. Valverde, P. Canizares, M. R. Sun Kou, C. B. Molina

Producción científica: Contribución a una revistaArtículorevisión exhaustiva

30 Citas (Scopus)


A commercial bentonite (primarily smectite) from Fischer Scientific Company (F bentonite) and a natural bentonite from Peru (P bentonite) were used in the preparation of pillared clays with polyoxymetal cations of Al that were subsequently modified with Ce and La. Several Al/metal ratios (5 and 9) were used to investigate the effects on the thermal and hydrothermal stability of these synthetic clays. The structure of these materials was studied by X-ray diffraction. Isotherms were determined by N2 adsorption. Thermal stability was determined using thermogravimetric (TG) measurements and ammonia-TPD (temperature programmed desorption) was used to obtain acidity data. These materials exhibited basal spacings from 16 to 20 Å, with surface areas from 239 to 347 m2 g-1, with microporosity contributing from 50 to 80% of the total surface area. Pillared clays prepared from F bentonite generally showed larger basal spacings and surface areas than those prepared from P bentonite. Pillared clays modified with Ce or La did not show any apparent structural changes relative to the Al-pillared clays. Pillared clays modified with Ce and La had similar acid properties as Al-pillared clays. In contrast, the thermal and hydrothermal stabilities of these materials were greater than Al-pillared clays. However, Ce-pillared clay appears to be more effective than La-pillared clay in delaying the dehydroxylation of pillared clays with increasing temperature. The intercalation of Ce and La into Al-pillared clays improved the thermal stability, which may increase the utility of these materials as catalysts.

Idioma originalInglés
Páginas (desde-hasta)424-432
Número de páginas9
PublicaciónClays and Clay Minerals
EstadoPublicada - 2000
Publicado de forma externa


Profundice en los temas de investigación de 'Enhanced thermal stability of A1-pillared smectites modified with Ce and La'. En conjunto forman una huella única.

Citar esto